A-2480

Name: TINOX A-2480 Fiber-grade anatase titanium dioxide pigment
Brand: TINOX
SKU: A-2480

Polyamide fiber-grade anatase TiO2 for PA6/PA66 delustering and high-load masterbatches

TINOX A-2480 is a sulfate-process anatase TiO2 with a multilayer aluminium, phosphorus and manganese coating plus organic treatment. It is designed for PA6/PA66 fiber delustering and high-concentration polyamide masterbatches, with low chromophoric trace elements, high aqueous-extract resistivity and stable spinning performance.

Key properties

Uniform delustering with a soft matte appearanceGood dispersion in water, caprolactam and polymer meltMultilayer Al / P / Mn coating with organic treatmentVery low iron, chromium and vanadiumAqueous-extract resistivity >= 100 ohm*mLow abrasion on spinning and textile equipment

↓ Download TDS Request sample Get a quote →

↓ Click to download TDS — A-2480

Download TDS — A-2480→Request a free sample→Get a price quote→Grade selection guide→All TDS downloads→

Responds within 24 hours

Technical specifications

Parameter	Value
Crystal form	Anatase
TiO2 content [%]	>= 95.0 (typical 95.5)
Whiteness, blue light [%]	>= 85 (typical 89)
pH value, aqueous suspension	7.0-8.5
Resistivity, aqueous extract [ohm*m]	>= 100
Matter volatile at 105 C [%]	<= 0.5 (typical 0.21)
Matter soluble in water [%]	<= 0.5 (typical 0.1)
Residue on sieve, 45 um [%]	<= 0.01 (typical 0.01)
Iron, as Fe2O3 [ppm]	<= 45 (typical 10)
Inorganic surface treatment	Al, P, Mn
Organic surface treatment	Present
Recommended dosage	0.2-0.5% polymerization; 0.2-0.8% semi-dull; 1.5-2.0% full-dull; 30-40% fiber masterbatch

Values represent typical results. Tinox Chemie GmbH reserves the right to update specifications. For the latest certified data, download the TDS.

Get the official TDS

Download the complete Technical Data Sheet — includes all certified parameters and test conditions. — A-2480

↓ Download TDS — A-2480